EO-84M-1HTK

ComponentsoneViscosity/25 ° C, cp40000-50000Storage condition: 20 ° C3monthRecommended curing conditionsonehrs@one50 °Cone5min@175 °Cappearancesilveryproportionthree point twoHardness, ShoreD-90Shear strength, psione thousand and six hundredGlass transition temperature (Tg) ° Cone hundred

EO-84M-1T

ComponentsoneViscosity/25 ° C, cp40000-60000Operating time 25 ° C (one00g)30daysRecommended curing conditionsonehrs@one50 °C15min@175 °Cappearancesilveryproportionthree point nineHardness, ShoreD-88Shear strength, psione thousand and six hundredGlass transition temperature (Tg) ° Cone hun

EO-98HT

ComponentsoneViscosity/25 ° C, cp35000-55000Operating time 25 ° C (one00g)30daysRecommended curing conditions5min@one50 °C30min@one25 °Cappearancesilveryproportionthree point fiveHardness, ShoreD-85Shear strength, psione thousand and two hundredGlass transition temperature (Tg) ° Cone hun

EO-97M

ComponentsoneViscosity/25 ° C, cp8000-one2000Operating time 25 ° C (one00g)20daysRecommended curing conditionsone-2min@175 °C ＜ 5min@160 °C5-10min@150 °C30-45min@125 °Cappearancesilveryproportionthree point twoHardness, ShoreD-89Shear strength, psione thousand and thre

EO-32HTK

ComponentstwoWeight mixing ratio100/twoViscosity/two5 ° C, cp40000-50000Operating time two5 ° C (100g)2daysRecommended curing conditions15min@150 °C 30min@120 °C2-3hrs@80-90 °Cappearancesilveryproportionthree point sevenHardness, ShoreD-85Shear strength, psione thousandGlass t

EO-21

ComponentstwoWeight mixing ratioone00/4Viscosity/two5 ° C, cp30000 - 40000Operating time two5 ° C (one00g) hoursoneRecommended curing conditionsonehrs@100 °Ctwo4-48hrs@25 °CappearancesilveryproportionthreeHardness, ShoreD-84Shear strength, psione thousand and seven hundredGlass transition temper

EO-20S

ComponentstwoWeight mixing ratio1/1Viscosity/two5 ° C, cptwo000 - thirty00Operating time two5 ° C (one hundredg) hoursforty-eightRecommended curing conditions5-6min@150 °C 15-20min@120 °C 45-50min@one hundred °C90-one hundredmin@80 °Cappearancesilveryproport

EO-31FL

ComponentstwoWeight mixing ratio1/1Viscosity/two5 ° C, cpPaste like substanceOperating time two5 ° C (ten0g) hours＞3Recommended curing conditionstwohrs@70-90 °C 4hrs@60 °C48hrs@25 °Cappearancesilveryproportionthree point twoHardness, ShoreA-65Shear strength, psisix hundredGlass tra

EO-30FST

ComponentstwoWeight mixing ratio100/100Viscosity/two5 ° C, cpPaste like substanceOperating time two5 ° C (100g)8-1twominRecommended curing conditions15-30min@65 °C24hrs@25 °Cappearancesilveryproportiontwo point fourHardness, ShoreD-70Shear strength, psione thousand and four hundredGlass tr

EO-30M-1

ComponentstwoWeight mixing ratio100/100Viscosity/two5 ° C, cpPaste like substanceOperating time two5 ° C (100g) hours3-4Recommended curing conditionstwohrs@100 °C24-48hrs@25 °Cappearancesilveryproportionthree point twoHardness, ShoreD-72Shear strength, psione thousand and seven hundredGlass tran

EO-23M

ComponentstwoWeight mixing ratioone00/4Viscosity/two5 ° C, cpfive thousandOperating time two5 ° C (one00g) hoursoneRecommended curing conditionstwohrs@80 °C24-48hrs@25 °Cappearancesilveryproportiontwo point nineHardness, ShoreD-84Shear strength, psione thousand and seven hundredGlass transition

EO-21M-5

ComponentstwoWeight mixing ratio100/10Viscosity/two5 ° C, cp1000 - 1500Operating time two5 ° C (100g) hours3-4Recommended curing conditions1hrs@100 °C8hrs@80 °Cappearancesilveryproportiontwo point sevenHardness, ShoreD-75Shear strength, psione thousand and one hundredGlass transition temperature

EO-20E

ComponentstwoWeight mixing ratio1/1Viscosity/two5 ° C, cptwo000 - 4000Operating time two5 ° C (one hundredg) hoursforty-eightRecommended curing conditions5-6min@150 °C 15-20min@120 °C 120-150min@one hundred °C180-200min@80 °Cappearancesilveryproportiontwo po